dc.contributor.authorRehana Akter Ruma & Md Shahidul Islam K. A. Khan, Ariful Islam, Bithi Paul, N. I. Khan, Md. Ohiduzzaman, Sazzad Hossain, S. R. Rasel-
dc.date.accessioned2023-11-12T07:44:53Z-
dc.date.available2023-11-12T07:44:53Z-
dc.date.issued2023-09-03-
dc.identifier.urihttp://dspace.aiub.edu:8080/jspui/handle/123456789/1807-
dc.description.abstractSpinel ferrite nanoparticles (NPs) are potential candidates due to their tremendous electrical and magnetic properties. Here, magnetic and physical features of stoichiometry Mg0.6-xCoxZn0.4(Fe1.5Cr0.5)O4 ferrite NPs have been studied where different cobalt content was used. The average particle size was calculated at 4–6 nm. NPs were probed by X-ray diffraction (XRD), vibrating sample magnetometer (VSM), and FT-IR spectroscopy. The molecular vibration band at 560 cm−1 is accounted for the metal–oxygen bond stretching at the tetrahedral site of NPs. The crystal structure of NPs was confirmed by XRD analysis. The magnetic parameters have been decreased for the cobalt content x = 0.2 on ferrite NPs which further increased on replacing magnesium ions with nonmagnetic cobalt ions for higher cobalt concentrations. Moreover, high saturation magnetization and coercivity were observed at 52.29 emu/g and 212 Oe for 0.00 and 0.6 cobalt contents, respectively, on ferrite NPs. In this study, sol–gel method provides an easy synthesis process of Co-doped ferrite nanoparticles at low temperature.en_US
dc.publisherSpringer, Singaporeen_US
dc.subjectFerrite Nanoparticlesen_US
dc.titleA Study on Structural and Magnetic Properties of Magnesium Cobalt Zinc Mg0.6-xCoxZn0.4 (Fe1.5Cr0.5)O4 (x = 0.0, 0.2, 0.4, 0.6) Ferrite Nanoparticlesen_US
dc.typeBook chapteren_US
Appears in Collections:Publication: Conference

Files in This Item:
File Description SizeFormat 
Chapter-2.docx4.06 MBMicrosoft Word XMLView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.